Synthesis of Nano-Crystalline Tin Dioxide and its Effect on Calcination

Abstract

Nitrate-citrate gel-combustion method was used in this study to prepare nano-crystalline tin dioxide. The samples were calcined at a temperature range of 543-1173 K. The prepared powder was characterized by SEM, TEM and X-ray diffraction. On increasing the temperature with limited supply of air (calcination), there is a systematic increase in tin content accompanied by a reduction in oxygen. The tetragonal nano tin structure formed during the process has about 20 nm in lateral size. With increase in calcination temperature, the carbon content systematically decreased.